303 vlekvrye staal vierkante staaf
Kort beskrywing:
Sakysteel is vervaardiger en verskaffers van ronde plat vierkantige seshoekstaaf in China, gespesialiseerd in die navorsing, ontwikkeling en produksie van 303Vlekvrye staal vierkante staaf;
| Spesifikasies van 303 vlekvrye staal vierkantige staaf: |
| Standaard | ASTM A276, A484, A479, A580, A582, JIS G4303, JIS G4311, DIN 1654-5, DIN 17440, KS D3706, GB/T 1220 |
| Materiaal | 201,202,205,XM-19 ens. 301,303,304,304L,304H,309S,310S,314,316,316L,316Ti,317,321,321H,329,330,348 ens. 409,410,416,420,430,430F,431,440 2205,2507,S31803,2209,630,631,15-5PH,17-4PH,17-7PH,904L,F51,F55, ens,253. |
| Oppervlakte | Helder gepoleer, haarlyn, gepekel |
| Tegnologie | Koud getrek, gesmee |
| Spesifikasies | 10*10mm-100*100mm |
| Verdraagsaamheid | soos vereis |
| Vlekvrye staal vierkantige staaf groottes: |
| 10*10 mm (2/5”) | 11*11mm | 12*12mm | 13*13mm | 14*14mm | 15*15 mm (3/5”) |
| 16*16mm | 17*17mm | 18*18mm | 19*19mm | 20*20 mm | 21*21 mm |
| 22*22 mm | 24*24 mm | 25*25 mm(1”) | 26*26mm | 28*28mm | 30*30 mm (1-1/5”) |
| 32*32 mm | 34*34 mm | 35*35 mm (1-1/5”) | 38*38mm | 40*40 mm (1-1/5”) | 42*42 mm |
| 45*45 mm (1-4/5”) | 48*48mm | 50*50 mm(2”) | 53*53 mm | 56*56 mm | 60*60 mm (2-2/5”) |
| 63*63 mm | 67*67 mm | 70*70 mm (2-4/5”) | 75*75 mm(3”) | 80*80 mm (3-1/5”) | 85*85 mm (3-2/5”) |
| 90*90 mm (3-3/5”) | 95*95 mm (3-4/5”) | 100*100mm(4”) |
| Voordeel: |
1: Vlekvrye staal van hoë gehalte met billike prys.
2: Wye uitstekende ervarings met na-verkope diens.
3: Elke proses sal nagegaan word deur verantwoordelike QC wat die kwaliteit van elke produk verseker.
4: Professionele verpakkingspanne wat elke verpakking veilig hou.
5: Proefbestelling kan binne een week gedoen word.
6: Monsters kan verskaf word as u vereiste.
| SS bar Verpakking: |
Sakysteel SS vierkantige stawe word verpak en gemerk volgens die regulasies en klante se versoeke.Groot sorg word getref om enige skade wat andersins tydens berging of vervoer veroorsaak kan word, te vermy.
| Meer grade vlekvrye staal vierkantige staaf: |
| Tik | Graad | Graad | Chemiese komponent % | ||||
| Austenitiese vlekvrye staal | C | Cr | Ni | Mn | |||
| 201 | 1Cr17Mn6Ni5N | 0,15 | 16.00-18.00 | 3,50-5,50 | 5,50-7,50 | ||
| 201L | 03Cr17Mn6Ni5N | 0,030 | 16.00-18.00 | 3,50-5,50 | 5,50-7,50 | ||
| 202 | 1Cr18Mn8Ni5N | 0,15 | 17.00-19.00 | 4.00-6.00 | 7.50-10.00 | ||
| 204 | 03Cr16Mn8Ni2N | 0,030 | 15.00-17.00 | 1,50-3,50 | 7.00-9.00 | ||
| 301 | 1Cr17Ni7 | 0,15 | 16.00-18.00 | 6.00-8.00 | 2.00 | ||
| 302 | 1Cr18Ni9 | 0,15 | 17.00-19.00 | 8.00-10.00 | 2.00 | ||
| 303 | Y1Cr18Ni9 | 0,15 | 17.00-19.00 | 8.00-10.00 | 2.00 | ||
| 303se | Y1Cr18Ni9Se | 0,15 | 17.00-19.00 | 8.00-10.00 | 2.00 | ||
| 304 | 0Cr18Ni9 | 0,07 | 17.00-19.00 | 8.00-10.00 | 2.00 | ||
| 304L | 00Cr19Ni10 | 0,030 | 18.00-20.00 | 8.00-10.00 | 2.00 | ||
| 304N1 | 0Cr19Ni9N | 0,08 | 18.00-20.00 | 7.00-10.50 | 2.00 | ||
| 304N2 | 0Cr18Ni10NbN | 0,08 | 18.00-20.00 | 7.50-10.50 | 2.00 | ||
| 304LN | 00Cr18Ni10N | 0,030 | 17.00-19.00 | 8.50-11.50 | 2.00 | ||
| 305 | 1Cr18Ni12 | 0.12 | 17.00-19.00 | 10.50-13.00 | 2.00 | ||
| 309S | 0Cr23Ni13 | 0,08 | 22.00-24.00 | 12.00-15.00 | 2.00 | ||
| 310S | 0Cr25Ni20 | 0,08 | 24.00-26.00 | 19.00-22.00 | 2.00 | ||
| 316 | 0Cr17Ni12Mo2 | 0,08 | 16.00-18.50 | 10.00-14.00 | 2.00 | ||
| 316L | 00Cr17Ni14Mo2 | 0,030 | 16.00-18.00 | 12.00-15.00 | 2.00 | ||
| 316N | 0Cr17Ni12Mo2N | 0,08 | 16.00-18.00 | 10.00-14.00 | 2.00 | ||
| 316N | 00Cr17Ni13Mo2N | 0,030 | 16.00-18.50 | 10.50-14.50 | 2.00 | ||
| 316J1 | 0Cr18Ni12Mo2Cu2 | 0,08 | 17.00-19.00 | 10.00-14.50 | 2.00 | ||
| 316J1L | 00Cr18Ni14Mo2Cu2 | 0,030 | 17.00-19.00 | 12.00-16.00 | 2.00 | ||
| 317 | 0Cr19Ni13Mo3 | 0.12 | 18.00-20.00 | 11.00-15.00 | 2.00 | ||
| 317L | 00Cr19Ni13Mo3 | 0,08 | 18.00-20.00 | 11.00-15.00 | 2.00 | ||
| 321 | 1Cr18Ni9Ti6 | 0.12 | 17.00-19.00 | 8.00-11.00 | 2.00 | ||
| 347 | 0Cr18Ni11Nb | 0,08 | 17.00-19.00 | 9.00-13.00 | 2.00 | ||
| XM7 | 0Cr18Ni9Cu3 | 0,08 | 17.00-19.00 | 8.50-10.50 | 2.00 | ||
| XM15J1 | 0Cr18Ni13Si4 | 0,08 | 15.00-20.00 | 11.50-15.00 | 2.00 | ||
| Ferriet vlekvrye staal | 405 | 0Cr13Al | 0,08 | 11.50-14.50 | 3) | 1.00 | 0,035 | 0,030 | - | 1.00 | - | - | Al 0,10-0,30 |
| 410L | 00Kr12 | 0,030 | 11.00-13.00 | 3) | 1.00 | 0,035 | 0,030 | - | 1.00 | - | - | - | |
| 430 | 1Kr17 | 0.12 | 16.00-18.00 | 3) | 1,25 | 0,035 | 0,030 | - | 0,75 | - | - | - | |
| 430F | Y1Cr17 | 0.12 | 16.00-18.00 | 3) | 1.00 | 0,035 | 0,15 | 1) | 1.00 | - | - | - | |
| 434 | 1Cr17Mo | 0.12 | 16.00-18.00 | 3) | 1.00 | 0,035 | 0,030 | 0,75-1,25 | 1.00 | - | - | - | |
| 447J1 | 00Cr30Mo2 | 0,010 | 28.50-32.00 | - | 0,40 | 0,035 | 0,030 | 1,50-2,50 | 0,40 | - | 0,015 | - | |
| XM27 | 00Cr27Mo | 0,010 | 25.00-27.50 | - | 0,40 | 0,035 | 0,030 | 0,75-1,50 | 0,40 | - | 0,015 | - |