303 Bar Sgwâr Dur Di-staen

Disgrifiad Byr:


  • Safon:ASTM, ASME, GB, ac ati
  • Gradd:301, 302, 304, 316, 316L,410, 420, 430,17-4PH etc.
  • Gorffen Arwyneb:du, llachar, caboledig ac ati
  • Technegau:Wedi'i rolio'n boeth, wedi'i dynnu'n oer, wedi'i ffugio, ac ati.
  • Manylion Cynnyrch

    Tagiau Cynnyrch

    Mae Sakysteel yn wneuthurwr bar hecsagon sgwâr fflat crwn a chyflenwyr mewn llestri, yn arbenigo mewn ymchwil, datblygu a chynhyrchu 303Bar Sgwâr Dur Di-staen;

    Manylebau 303 bar sgwâr dur di-staen :
    Safonol ASTM A276, A484, A479, A580, A582, JIS G4303, JIS G4311, DIN 1654-5, DIN 17440, KS D3706, GB / T 1220
    Deunydd 201,202,205, XM-19 ac ati.
    301,303,304,304L,304H,309S,310S,314,316,316L,316Ti,317,321,321H,329,330,348 ac ati.
    409,410,416,420,430,430F,431,440 2205,2507,S31803,2209,630,631,15-5PH,17-4PH,17-7PH,904L,F51,F55,253 ac ati.
    Arwyneb Gloyw sgleiniog, hairline, piclo
    Technoleg Oer Drawn, Forged
    Manylebau 10*10mm-100*100mm
    Goddefgarwch yn ôl yr angen

     

    Meintiau bar sgwâr dur di-staen:
    10*10mm(2/5”) 11*11mm 12*12mm 13*13mm 14*14mm 15*15mm(3/5”)
    16*16mm 17*17mm 18*18mm 19*19mm 20*20mm 21*21mm
    22*22mm 24*24mm 25*25mm(1”) 26*26mm 28*28mm 30*30mm(1-1/5”)
    32*32mm 34*34mm 35*35mm(1-1/5”) 38*38mm 40*40mm(1-1/5”) 42*42mm
    45*45mm(1-4/5”) 48*48mm 50*50mm(2”) 53*53mm 56*56mm 60*60mm(2-2/5”)
    63*63mm 67*67mm 70*70mm(2-4/5”) 75*75mm(3”) 80*80mm(3-1/5”) 85*85mm(3-2/5”)
    90*90mm(3-3/5”) 95*95mm(3-4/5”) 100*100mm(4”)      

     

    Mantais:

    1: Dur di-staen o ansawdd uchel gyda phris rhesymol.
    2: Profiadau rhagorol eang gyda gwasanaeth ôl-werthu.
    3: Bydd pob proses yn cael ei gwirio gan QC cyfrifol sy'n yswirio ansawdd pob cynnyrch.
    4: Timau pacio proffesiynol sy'n cadw pob pacio yn ddiogel.
    5: Gellir gwneud gorchymyn prawf mewn wythnos.
    6: Gellir darparu samplau fel eich gofyniad.

    Pecynnu bar SS:

    Mae bariau sgwâr Sakysteel SS yn cael eu pacio a'u labelu yn unol â'r rheoliadau a cheisiadau cwsmeriaid.Cymerir gofal mawr i osgoi unrhyw ddifrod a allai gael ei achosi fel arall wrth storio neu gludo.

    Pecyn Bar Sgwâr Dur Di-staen

    Mwy o raddau o far sgwâr dur di-staen:
    Math Gradd Gradd Cydran Cemegol %
    Dur di-staen austenitig     C Cr Ni Mn  
    201 1Cr17Mn6Ni5N 0.15 16.00-18.00 3.50-5.50 5.50-7.50  
    201L 03Cr17Mn6Ni5N 0.030 16.00-18.00 3.50-5.50 5.50-7.50  
    202 1Cr18Mn8Ni5N 0.15 17.00-19.00 4.00-6.00 7.50-10.00  
    204 03Cr16Mn8Ni2N 0.030 15.00-17.00 1.50-3.50 7.00-9.00  
    301 1Cr17Ni7 0.15 16.00-18.00 6.00-8.00 2.00  
    302 1Cr18Ni9 0.15 17.00-19.00 8.00-10.00 2.00  
    303 Y1Cr18Ni9 0.15 17.00-19.00 8.00-10.00 2.00  
    303se Y1Cr18Ni9Se 0.15 17.00-19.00 8.00-10.00 2.00  
    304 0Cr18Ni9 0.07 17.00-19.00 8.00-10.00 2.00  
    304L 00Cr19Ni10 0.030 18.00-20.00 8.00-10.00 2.00  
    304N1 0Cr19Ni9N 0.08 18.00-20.00 7.00-10.50 2.00  
    304N2 0Cr18Ni10NbN 0.08 18.00-20.00 7.50-10.50 2.00  
    304LN 00Cr18Ni10N 0.030 17.00-19.00 8.50-11.50 2.00  
    305 1Cr18Ni12 0.12 17.00-19.00 10.50-13.00 2.00  
    309S 0Cr23Ni13 0.08 22.00-24.00 12.00-15.00 2.00  
    310S 0Cr25Ni20 0.08 24.00-26.00 19.00-22.00 2.00  
    316 0Cr17Ni12Mo2 0.08 16.00-18.50 10.00-14.00 2.00  
    316L 00Cr17Ni14Mo2 0.030 16.00-18.00 12.00-15.00 2.00  
    316N 0Cr17Ni12Mo2N 0.08 16.00-18.00 10.00-14.00 2.00  
    316N 00Cr17Ni13Mo2N 0.030 16.00-18.50 10.50-14.50 2.00  
    316J1 0Cr18Ni12Mo2Cu2 0.08 17.00-19.00 10.00-14.50 2.00  
    316J1L 00Cr18Ni14Mo2Cu2 0.030 17.00-19.00 12.00-16.00 2.00  
    317 0Cr19Ni13Mo3 0.12 18.00-20.00 11.00-15.00 2.00  
    317L 00Cr19Ni13Mo3 0.08 18.00-20.00 11.00-15.00 2.00  
    321 1Cr18Ni9Ti6 0.12 17.00-19.00 8.00-11.00 2.00  
    347 0Cr18Ni11Nb 0.08 17.00-19.00 9.00-13.00 2.00  
    XM7 0Cr18Ni9Cu3 0.08 17.00-19.00 8.50-10.50 2.00  
    XM15J1 0Cr18Ni13Si4 0.08 15.00-20.00 11.50-15.00 2.00  
    Dur Di-staen Ferrite 405 0Cr13Al 0.08 11.50-14.50 3) 1.00 0.035 0.030 - 1.00 - - Al 0.10-0.30
    410L 00Cr12 0.030 11.00-13.00 3) 1.00 0.035 0.030 - 1.00 - - -
    430 1Cr17 0.12 16.00-18.00 3) 1.25 0.035 0.030 - 0.75 - - -
    430F Y1Cr17 0.12 16.00-18.00 3) 1.00 0.035 0.15 1) 1.00 - - -
    434 1Cr17Mo 0.12 16.00-18.00 3) 1.00 0.035 0.030 0.75-1.25 1.00 - - -
    447J1 00Cr30Mo2 0.010 28.50-32.00 - 0.40 0.035 0.030 1.50-2.50 0.40 - 0.015 -
    XM27 00Cr27Mo 0.010 25.00-27.50 - 0.40 0.035 0.030 0.75-1.50 0.40 - 0.015 -

     