303 roostevabast terasest ruudukujulise varda spetsifikatsioonid: |
Standard | ASTM A276, A484, A479, A580, A582, JIS G4303, JIS G4311, DIN 1654-5, DIN 17440, KS D3706, GB/T 1220 |
Materjal | 201,202,205,XM-19 jne. 301,303,304,304L,304H,309S,310S,314,316,316L, 316Ti, 317,321,321H, 329,330,348 jne. 409,410,416,420,430,430F,431,440 2205,2507,S31803,2209,630,631,15-5PH,17-4PH,17-7PH,904L,F51,F55,253. |
Pind | Poleeritud särav, juuksepiir, marineeritud |
Tehnoloogia | Külmtõmmatud, sepistatud |
Tehnilised andmed | 10*10mm-100*100mm |
Tolerantsus | nõutud |
Roostevabast terasest ruudukujulised varda suurused: |
10*10mm (2/5”) | 11*11mm | 12*12mm | 13*13mm | 14*14mm | 15*15mm (3/5”) |
16*16mm | 17*17mm | 18*18mm | 19*19mm | 20*20mm | 21*21mm |
22*22mm | 24*24mm | 25*25mm (1”) | 26*26mm | 28*28mm | 30*30mm (1-1/5”) |
32*32mm | 34*34mm | 35*35mm (1-1/5”) | 38*38mm | 40*40mm (1-1/5”) | 42*42mm |
45*45mm (1-4/5”) | 48*48mm | 50*50mm (2”) | 53*53mm | 56*56mm | 60*60mm (2-2/5”) |
63*63mm | 67*67mm | 70*70 mm (2-4/5”) | 75*75mm (3”) | 80*80mm (3-1/5”) | 85*85mm (3-2/5”) |
90*90mm (3-3/5”) | 95*95mm (3-4/5”) | 100*100mm (4”) |
Eelis: |
1: Kvaliteetne roostevaba teras mõistliku hinnaga.
2: laialdased suurepärased kogemused müügijärgse teenindusega.
3: iga protsessi kontrollib vastutav QC, mis tagab iga toote kvaliteedi.
4: professionaalsed pakkimismeeskonnad, kes hoiavad iga pakkimise ohutuna.
5: proovitellimuse saab teha ühe nädala jooksul.
6: proovid saab esitada vastavalt teie nõudele.
SS baari pakend: |
Sakysteel SS kandilised latid pakitakse ja märgistatakse vastavalt eeskirjadele ja kliendi soovidele.Pööratakse suurt tähelepanu sellele, et vältida kahjustusi, mis võivad muidu ladustamise või transportimise ajal tekkida.
Rohkem roostevabast terasest kandilise varda sorte: |
Tüüp | Hinne | Hinne | Keemiline komponent % | ||||
Austeniit roostevaba teras | C | Cr | Ni | Mn | |||
201 | 1Cr17Mn6Ni5N | 0,15 | 16.00-18.00 | 3.50-5.50 | 5.50-7.50 | ||
201L | 03Cr17Mn6Ni5N | 0,030 | 16.00-18.00 | 3.50-5.50 | 5.50-7.50 | ||
202 | 1Cr18Mn8Ni5N | 0,15 | 17.00-19.00 | 4.00-6.00 | 7.50-10.00 | ||
204 | 03Cr16Mn8Ni2N | 0,030 | 15.00-17.00 | 1.50-3.50 | 7.00-9.00 | ||
301 | 1Cr17Ni7 | 0,15 | 16.00-18.00 | 6.00-8.00 | 2.00 | ||
302 | 1Cr18Ni9 | 0,15 | 17.00-19.00 | 8.00-10.00 | 2.00 | ||
303 | Y1Cr18Ni9 | 0,15 | 17.00-19.00 | 8.00-10.00 | 2.00 | ||
303se | Y1Cr18Ni9Se | 0,15 | 17.00-19.00 | 8.00-10.00 | 2.00 | ||
304 | 0Cr18Ni9 | 0,07 | 17.00-19.00 | 8.00-10.00 | 2.00 | ||
304L | 00Cr19Ni10 | 0,030 | 18.00-20.00 | 8.00-10.00 | 2.00 | ||
304N1 | 0Cr19Ni9N | 0,08 | 18.00-20.00 | 7.00-10.50 | 2.00 | ||
304N2 | 0Cr18Ni10NbN | 0,08 | 18.00-20.00 | 7.50-10.50 | 2.00 | ||
304LN | 00Cr18Ni10N | 0,030 | 17.00-19.00 | 8.50-11.50 | 2.00 | ||
305 | 1Cr18Ni12 | 0.12 | 17.00-19.00 | 10.50-13.00 | 2.00 | ||
309S | 0Cr23Ni13 | 0,08 | 22.00-24.00 | 12.00-15.00 | 2.00 | ||
310S | 0Cr25Ni20 | 0,08 | 24.00-26.00 | 19.00-22.00 | 2.00 | ||
316 | 0Cr17Ni12Mo2 | 0,08 | 16.00-18.50 | 10.00-14.00 | 2.00 | ||
316L | 00Cr17Ni14Mo2 | 0,030 | 16.00-18.00 | 12.00-15.00 | 2.00 | ||
316N | 0Cr17Ni12Mo2N | 0,08 | 16.00-18.00 | 10.00-14.00 | 2.00 | ||
316N | 00Cr17Ni13Mo2N | 0,030 | 16.00-18.50 | 10.50-14.50 | 2.00 | ||
316J1 | 0Cr18Ni12Mo2Cu2 | 0,08 | 17.00-19.00 | 10.00-14.50 | 2.00 | ||
316J1L | 00Cr18Ni14Mo2Cu2 | 0,030 | 17.00-19.00 | 12.00-16.00 | 2.00 | ||
317 | 0Cr19Ni13Mo3 | 0.12 | 18.00-20.00 | 11.00-15.00 | 2.00 | ||
317L | 00Cr19Ni13Mo3 | 0,08 | 18.00-20.00 | 11.00-15.00 | 2.00 | ||
321 | 1Cr18Ni9Ti6 | 0.12 | 17.00-19.00 | 8.00-11.00 | 2.00 | ||
347 | 0Cr18Ni11Nb | 0,08 | 17.00-19.00 | 9.00-13.00 | 2.00 | ||
XM7 | 0Cr18Ni9Cu3 | 0,08 | 17.00-19.00 | 8.50-10.50 | 2.00 | ||
XM15J1 | 0Cr18Ni13Si4 | 0,08 | 15.00-20.00 | 11.50-15.00 | 2.00 |
Ferriit roostevaba teras | 405 | 0Cr13Al | 0,08 | 11.50-14.50 | 3) | 1.00 | 0,035 | 0,030 | - | 1.00 | - | - | Al 0,10-0,30 |
410L | 00Cr12 | 0,030 | 11.00-13.00 | 3) | 1.00 | 0,035 | 0,030 | - | 1.00 | - | - | - | |
430 | 1Cr17 | 0.12 | 16.00-18.00 | 3) | 1.25 | 0,035 | 0,030 | - | 0,75 | - | - | - | |
430F | Y1Cr17 | 0.12 | 16.00-18.00 | 3) | 1.00 | 0,035 | 0,15 | 1) | 1.00 | - | - | - | |
434 | 1kr17 kuu | 0.12 | 16.00-18.00 | 3) | 1.00 | 0,035 | 0,030 | 0,75-1,25 | 1.00 | - | - | - | |
447J1 | 00Cr30Mo2 | 0,010 | 28.50-32.00 | - | 0,40 | 0,035 | 0,030 | 1.50-2.50 | 0,40 | - | 0,015 | - | |
XM27 | 00Cr27Mo | 0,010 | 25.00-27.50 | - | 0,40 | 0,035 | 0,030 | 0,75-1,50 | 0,40 | - | 0,015 | - |