Gawo la Stainless Steel T
Kufotokozera Kwachidule:
Stainless steel T bar, T gawo kapena Tee mbiri yokhala ndi kalasi 201,303,304,304L,316,316L,316TI,321,310S,410,430
| Zofotokozera zaT bar yachitsulo chosapanga dzimbiri: |
| Standard | ASTM A276, A484, A479, A580, A582, JIS G4303, JIS G4311,DIN 1654-5,DIN 17440,KS D3706,GB/T 1220 |
| Zakuthupi | 201,202,205,XM-19 etc. 301,303,304,304L,304H,309S,310S,314,316,316L,316Ti,317,321,321H,329,330,348 etc. 409,410,416,420,430,430F,431,440 2205,2507,S31803,2209,630,631,15-5PH,17-4PH,17-7PH,904L,F51,F55,253MA etc. |
| Pamwamba | Wowala, Wopukutira, Wokazinga, Wosenda, Wakuda, Akupera, Chigayo, Mirror, Tsitsi etc. |
| Zamakono | Zokoka Zozizira, Zotenthedwa Zotentha, Zopangidwa |
| Zofotokozera | monga pakufunika |
| Kulekerera | H9, H11, H13, K9, K11, K13 kapena pakufunika |
| Zogulitsa za Stainless Steel T kuchokera ku Sakysteel: |
 Opanga Stainless Steel T Section |  Stainless Steel T Section ogulitsa |
| Kulemera kwaT bar yachitsulo chosapanga dzimbiri |
| Chitsanzo | Kulemera | Chitsanzo | Kulemera |
| 100*50*5*7 | 9.54 | 344*354*16*16 | 131 |
| 100*100*6*8 | 17.2 | 346*174*6*9 | 41.8 |
| 125*60*6*8 | 13.3 | 350*175*7*11 | 50 |
| 125*125*6.5*9 | 23.8 | 344*348*10*16 | 115 |
| 148*100*6*9 | 21.4 | 350*350*12*19 | 137 |
| 150*75*5*7 | 14.3 | 388*402*15*15 | 141 |
| 150*150*7*10 | 31.9 | 390*300*10*16 | 107 |
| 175*90*5*8 | 18.2 | 394*398*11*18 | 147 |
| 175*175*7.5*11 | 40.3 | 400*150*8*13 | 55.8 |
| 194*150*6*9 | 31.2 | 396*199*7*11 | 56.7 |
| 198*99*4.5*7 | 18.5 | 400*200*8*13 | 66 |
| 200*100*5.5*8 | 21.7 | 400*400*13*21 | 172 |
| 200*200*8*12 | 50.5 | 400*408*21*21 | 197 |
| 200*204*12*12 | 72.28 | 414*405*18*28 | 233 |
| 244*175*7*11 | 44.1 | 440*300*11*18 | 124 |
| 244*252*11*11 | 64.4 | 446*199*7*11 | 66.7 |
| 248*124*5*8 | 25.8 | 450*200*9-14 | 76.5 |
| 250*125*6*9 | 29.7 | 482*300*11*15 | 115 |
| 250*250*9*14 | 72.4 | 488*300*11*18 | 129 |
| 250*255*14*14 | 82.2 | 496*199*9*14 | 79.5 |
| 294*200*8*12 | 57.3 | 500*200*10*16 | 89.6 |
| 300*150*6.5*9 | 37.3 | 582*300*12*17 | 137 |
| 294*302*12*12 | 85 | 588*300*12*20 | 151 |
| 300*300*10*15 | 94.5 | 596*199*10*15 | 95.1 |
| 300*305*15*15 | 106 | 600*200*11*17 | 106 |
| 338*351*13*13 | 106 | 700*300*13*24 | 185 |
| 340*250*9*14 | 79.7 |
| More kalasi yaT bar yachitsulo chosapanga dzimbiri: |
| Mtundu | Gulu | Gulu | Chemical Component% | ||||||||||
| C | Cr | Ni | Mn | P | S | Mo | Si | Cu | N | Zina | |||
| Chitsulo chosapanga dzimbiri cha Austenitic | 201 | Mtengo wa 1Cr17Mn6Ni5N | 0.15 | 16.00-18.00 | 3.50-5.50 | 5.50-7.50 | 0.060 | 0.030 | - | 1.00 | - | 0.25 | - |
| 201l pa | Mtengo wa 03Cr17Mn6Ni5N | 0.030 | 16.00-18.00 | 3.50-5.50 | 5.50-7.50 | 0.060 | 0.030 | 1.00 | 0.25 | ||||
| 202 | Mtengo wa 1Cr18Mn8Ni5N | 0.15 | 17.00-19.00 | 4.00-6.00 | 7.50-10.00 | 0.060 | 0.030 | 1.00 | - | 0.25 | - | ||
| 204 | Mtengo wa 03Cr16Mn8Ni2N | 0.030 | 15.00-17.00 | 1.50-3.50 | 7.00-9.00 | 0.15-0.30 | |||||||
| Mtengo wa 1Cr18Mn10Ni5Mo3N | 0.10 | 17.00-19.00 | 4.00-6.00 | 8.50-12.00 | 2.80-3.50 | 0.20-0.30 | |||||||
| 2Cr13Mn9Ni4 | 0.15-0.25 | 12.00-14.00 | 3.70-5.00 | 8.00-10.00 | |||||||||
| Mtengo wa 2Cr15Mn15Ni2N | 0.15-0.25 | 14.00-16.00 | 1.50-3.00 | 14.00-16.00 | 0.15-0.30 | ||||||||
| Mtengo wa 1Cr18Mn10Ni5Mo3N | 0.15 | 17.00-19.00 | 4.00-6.00 | 8.50-12.00 | 0.060 | 0.030 | 2.8-3.5 | 1.00 | - | 0.20-0.30 | - | ||
| 301 | 1Cr17Ni7 | 0.15 | 16.00-18.00 | 6.00-8.00 | 2.00 | 0.065 | 0.030 | - | 1.00 | - | - | - | |
| 302 | 1Cr18Ni9 | 0.15 | 17.00-19.00 | 8.00-10.00 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
| 303 | Y1Cr18Ni9 | 0.15 | 17.00-19.00 | 8.00-10.00 | 2.00 | 0.20 | 0.030 | 1) | 1.00 | - | - | - | |
| 303 ndi | Y1Cr18Ni9Se | 0.15 | 17.00-19.00 | 8.00-10.00 | 2.00 | 0.20 | 0.030 | - | 1.00 | - | - | Se=0.15 | |
| 304 | 0Cr18Ni9 | 0.07 | 17.00-19.00 | 8.00-10.00 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
| 304l pa | 00Cr19Ni10 | 0.030 | 18.00-20.00 | 8.00-10.00 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
| Mtengo wa 304N1 | 0Cr19Ni9N | 0.08 | 18.00-20.00 | 7.00-10.50 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | 0.10-0.25 | - | |
| Mtengo wa 304N2 | Mtengo wa 0Cr18Ni10NbN | 0.08 | 18.00-20.00 | 7.50-10.50 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | 0.15-0.30 | Nb=0.15 | |
| 304LN | Mtengo wa 00Cr18Ni10N | 0.030 | 17.00-19.00 | 8.50-11.50 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | 0.12-0.22 | - | |
| 305 | 1Cr18Ni12 | 0.12 | 17.00-19.00 | 10.50-13.00 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
| 309s ndi | 0Cr23Ni13 | 0.08 | 22.00-24.00 | 12.00-15.00 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
| 310s | 0Cr25Ni20 | 0.08 | 24.00-26.00 | 19.00-22.00 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
| 316 | Chithunzi cha 0Cr17Ni12Mo2 | 0.08 | 16.00-18.50 | 10.00-14.00 | 2.00 | 0.035 | 0.030 | 2.00-3.00 | 1.00 | - | - | - | |
| 1Cr18Ni12Mo2Ti6) | 0.12 | 16.00-19.00 | 11.00-14.00 | 2.00 | 0.035 | 0.030 | 1.80-2.50 | 1.00 | - | - | Ti5(C%-0.02)~0.08 | ||
| Mtengo wa 0Cr18Ni12Mo2Ti | 0.08 | 16.00-19.00 | 11.00-14.00 | 2.00 | 0.035 | 0.030 | 1.80-2.50 | 1.00 | - | - | Ti5*C% -0.70 | ||
| 316l ndi | Chithunzi cha 00Cr17Ni14Mo2 | 0.030 | 16.00-18.00 | 12.00-15.00 | 2.00 | 0.035 | 0.030 | 2.00-3.00 | 1.00 | - | - | - | |
| 316N | Mtengo wa 0Cr17Ni12Mo2N | 0.08 | 16.00-18.00 | 10.00-14.00 | 2.00 | 0.035 | 0.030 | 2.00-3.00 | 1.00 | - | 0.10-0.22 | - | |
| 316N | Mtengo wa 00Cr17Ni13Mo2N | 0.030 | 16.00-18.50 | 10.50-14.50 | 2.00 | 0.035 | 0.030 | 2.00-3.00 | 1.00 | - | 0.12-0.22 | - | |
| 316j1 | Chithunzi cha 0Cr18Ni12Mo2Cu2 | 0.08 | 17.00-19.00 | 10.00-14.50 | 2.00 | 0.035 | 0.030 | 1.20-2.75 | 1.00 | 1.00-2.50 | - | - | |
| 316J1L | Mtengo wa 00Cr18Ni14Mo2Cu2 | 0.030 | 17.00-19.00 | 12.00-16.00 | 2.00 | 0.035 | 0.030 | 1.20-2.75 | 1.00 | 1.00-2.50 | - | - | |
| 317 | Chithunzi cha 0Cr19Ni13Mo3 | 0.12 | 18.00-20.00 | 11.00-15.00 | 2.00 | 0.035 | 0.030 | 3.00-4.00 | 1.00 | - | - | - | |
| 317l ndi | Mtengo wa 00Cr19Ni13Mo3 | 0.08 | 18.00-20.00 | 11.00-15.00 | 2.00 | 0.035 | 0.030 | 3.00-4.00 | 1.00 | - | - | - | |
| Chithunzi cha 1Cr18Ni12Mo3Ti6 | 0.12 | 16.00-19.00 | 11.00-14.00 | 2.00 | 0.035 | 0.030 | 2.50-3.50 | 1.00 | - | - | Ti5(C%-0.02)~0.08 | ||
| Mtengo wa 0Cr18Ni12Mo3Ti | 0.08 | 16.00-19.00 | 11.00-14.00 | 2.00 | 0.035 | 0.030 | 2.50-3.50 | 1.00 | - | - | Ti5*C% -0.70 | ||
| 317j1 | Chithunzi cha 0Cr18Ni16Mo5 | 0.040 | 16.00-19.00 | 15.00-17.00 | 2.00 | 0.035 | 0.030 | 4.00-6.00 | 1.00 | - | - | - | |
| 321 | 1Cr18Ni9Ti6 | 0.12 | 17.00-19.00 | 8.00-11.00 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | - | Ti5(C%-0.02)~0.08 | |
| 0Cr18Ni10Ti | 0.08 | 17.00-19.00 | 9.00-12.00 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | - | Ti=5*C% | ||
| 347 | Mtengo wa 0Cr18Ni11Nb | 0.08 | 17.00-19.00 | 9.00-13.00 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | - | Nb=10*C% | |
| XM7 | 0Cr18Ni9Cu3 | 0.08 | 17.00-19.00 | 8.50-10.50 | 2.00 | 0.035 | 0.030 | - | 1.00 | 3.00-4.00 | - | - | |
| XM15J1 | 0Cr18Ni13Si4 | 0.08 | 15.00-20.00 | 11.50-15.00 | 2.00 | 0.035 | 0.030 | - | 3.00-5.00 | - | - | 2) | |
| Austenite | 329j1 pa | Mtengo wa 0Cr26Ni5Mo2 | 0.08 | 23.00-28.00 | 3.00-6.00 | 1.50 | 0.035 | 0.030 | 1.00-3.00 | 1.00 | - | - | 2) |
| | | Chithunzi cha 1Cr18Ni11Si4AlTi | 0.10-0.18 | 17.50-19.50 | 10-120.. | 0.80 | 0.035 | 0.030 | - | 3.40-4.00 | - | - | Al 0.10-0.30;Ndi 0.40-0.70 | |
| Ferrite Stainless Steel | 00Cr18Ni5MoSi2 | 0.030 | 18.00-19.50 | 4.50-5.50 | 1.00-2.00 | 0.035 | 0.030 | 2.50-3.00 | 1.30-2.00 | - | - | - | |
| Ferrite Stainless Steel | 405 | 0Cr13Al | 0.08 | 11.50-14.50 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | Pa 0.10-0.30 |
| 410l pa | 00Cr12 | 0.030 | 11.00-13.00 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
| 430 | 1Kr17 | 0.12 | 16.00-18.00 | 3) | 1.25 | 0.035 | 0.030 | - | 0.75 | - | - | - | |
| 430F | Y1Cr17 | 0.12 | 16.00-18.00 | 3) | 1.00 | 0.035 | 0.15 | 1) | 1.00 | - | - | - | |
| 434 | 1Cr17Mo | 0.12 | 16.00-18.00 | 3) | 1.00 | 0.035 | 0.030 | 0.75-1.25 | 1.00 | - | - | - | |
| 447j1 | 00Cr30Mo2 | 0.010 | 28.50-32.00 | - | 0.40 | 0.035 | 0.030 | 1.50-2.50 | 0.40 | - | =0.015 | - | |
| XM27 | 00Cr27Mo | 0.010 | 25.00-27.50 | - | 0.40 | 0.035 | 0.030 | 0.75-1.50 | 0.40 | - | =0.015 | - | |
| Martensite chitsulo chosapanga dzimbiri | 403 | 1Kr12 | 0.15 | 11.50-13.00 | 3) | 1.00 | 0.035 | 0.030 | - | 0.50 | - | - | - |
| 410 | 1Kr13 | 0.15 | 11.50-13.50 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
| 405 | 0Kr13 | 0.08 | 11.50-13.50 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
| 416 | Y1Cr13 | 0.15 | 12.00-14.00 | 3) | 1.25 | 0.035 | 0.15 | 1) | 1.00 | - | - | - | |
| 410j1 | 1Cr13Mo | 0.08-0.18 | 11.50-14.00 | 3) | 1.00 | 0.035 | 0.030 | 0.30-0.60 | 0.60 | - | - | - | |
| 420j1 | 2Kr13 | 0.16-0.25 | 12.00-14.00 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
| 420j2 | 3Kr13 | 0.26-0.35 | 12.00-14.00 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
| 420F | Y3Cr13 | 0.26-0.40 | 12.00-14.00 | 3) | 1.25 | 0.035 | 0.15 | 1) | 1.00 | - | - | - | |
| 3Cr13Mo | 0.28-0.35 | 12.00-14.00 | 3) | 1.00 | 0.035 | 0.030 | 0.50-1.00 | 0.80 | - | - | - | ||
| 4Kr13 | 0.36-0.45 | 12.00-14.00 | 3) | 0.80 | 0.035 | 0.030 | - | 0.60 | - | - | - | ||
| 431 | 1Cr17Ni2 | 0.11-0.17 | 16.00-18.00 | 1.50-2.50 | 0.80 | 0.035 | 0.030 | - | 0.80 | - | - | - | |
| 440A | 7Kr17 | 0.60-0.75 | 16.00-18.00 | 3) | 1.00 | 0.035 | 0.030 | 4) | 1.00 | - | - | - | |
| 440b | 8Kr17 | 0.75-0.95 | 16.00-18.00 | 3) | 1.00 | 0.035 | 0.030 | 4) | 1.00 | - | - | - | |
| 9 mkh18 | 0.90-1.00 | 17.00-19.00 | 3) | 0.80 | 0.035 | 0.030 | 4) | 0.80 | - | - | - | ||
| 440C | 11Kr17 | 0.95-1.20 | 16.00-18.00 | 3) | 1.00 | 0.035 | 0.030 | 4) | 1.00 | - | - | - | |
| 440F | Y11Cr17 | 0.95-1.20 | 16.00-18.00 | 3) | 1.25 | 0.035 | 0.15 | 4) | 1.00 | - | - | - | |
| 9Cr18Mo | 0.95-1.10 | 16.00-18.00 | 3) | 0.80 | 0.035 | 0.030 | 0.40-0.70 | 0.80 | - | - | - | ||
| Mtengo wa 9Cr18MoV | 0.85-0.95 | 17.00-19.00 | 3) | 0.80 | 0.035 | 0.030 | 1.00-1.30 | 0.80 | - | - | V0.07-0.12 | ||
| PH Chitsulo chosapanga dzimbiri | 630 | Mtengo wa 0Cr17Ni4Cu4Nb | 0.07 | 15.50-17.50 | 6.50-7.50 | 1.00 | 0.035 | 0.030 | - | 1.00 | 3.00-5.00 | - | Nb 0.15-0.45 |
| 631 | 0Cr17Ni7Al | 0.09 | 16.00-18.00 | 6.50-7.50 | 1.00 | 0.035 | 0.030 | - | 1.00 | 0.50 | - | Al 0.75-1.50 | |