| Chiwonetsero cha Stainless Steel Coils One stop Service Showcase: |
| 430 pepala lachitsulo chosapanga dzimbiriChemical Composition ndi Mechanical properties: |
| C% | Si% | Mn% | P% | S% | Cr% | Ndi% | N% | Mo% | Ti% |
| 0.12 | 1.00 | 1.00 | 0.040 | 0.030 | 16.0-18.0 | 0.75 | - | - | - |
| T*S | Y*S | Kuuma | Elongation |
| (Mpa) | (Mpa) | HRB | HB | (%) |
| 520 | 205 | - | - | 40 |
| Wozizira Wokulungidwa430 zitsulo zosapanga dzimbiri: |
1. Gulu: 200 & 300 mndandanda
200 mndandanda: 201,202, J4
300 mndandanda: 301, 304, 304L, 321, 316L, 309, 310S
2. Standard: JIS, ASTM, AISI, GB, DIN, EN, nthawi zambiri timagwiritsa ntchito ASTM ndi GB Standard
3. Makulidwe: 0.14mm-3.0mm
4. M'lifupi: monga pakufunika
5. Pamwamba: 2B yatha, BA yatha
6. Kuuma: zofewa, 1/4H, 1/2H, FH
7. Makulidwe Kulekerera: +/-0.02mm
8. M'lifupi Kulekerera: +/-10mm(m'mphepete mwa mphero)
| Makalasi enanso a 430 ss sheet: |
| Mtundu | Gulu | Gulu | Chemical Component% |
| Chitsulo chosapanga dzimbiri cha Austenitic | | | C | Cr | Ni | Mn |
| 201 | Mtengo wa 1Cr17Mn6Ni5N | 0.15 | 16.00-18.00 | 3.50-5.50 | 5.50-7.50 |
| 201l pa | Mtengo wa 03Cr17Mn6Ni5N | 0.030 | 16.00-18.00 | 3.50-5.50 | 5.50-7.50 |
| 202 | Mtengo wa 1Cr18Mn8Ni5N | 0.15 | 17.00-19.00 | 4.00-6.00 | 7.50-10.00 |
| 204 | Mtengo wa 03Cr16Mn8Ni2N | 0.030 | 15.00-17.00 | 1.50-3.50 | 7.00-9.00 |
| Mtengo wa 1Cr18Mn10Ni5Mo3N | 0.10 | 17.00-19.00 | 4.00-6.00 | 8.50-12.00 |
| 2Cr13Mn9Ni4 | 0.15-0.25 | 12.00-14.00 | 3.70-5.00 | 8.00-10.00 |
| Mtengo wa 2Cr15Mn15Ni2N | 0.15-0.25 | 14.00-16.00 | 1.50-3.00 | 14.00-16.00 |
| Mtengo wa 1Cr18Mn10Ni5Mo3N | 0.15 | 17.00-19.00 | 4.00-6.00 | 8.50-12.00 |
| 301 | 1Cr17Ni7 | 0.15 | 16.00-18.00 | 6.00-8.00 | 2.00 |
| 302 | 1Cr18Ni9 | 0.15 | 17.00-19.00 | 8.00-10.00 | 2.00 |
| 303 | Y1Cr18Ni9 | 0.15 | 17.00-19.00 | 8.00-10.00 | 2.00 |
| 303 ndi | Y1Cr18Ni9Se | 0.15 | 17.00-19.00 | 8.00-10.00 | 2.00 |
| 304 | 0Cr18Ni9 | 0.07 | 17.00-19.00 | 8.00-10.00 | 2.00 |
| 304l pa | 00Cr19Ni10 | 0.030 | 18.00-20.00 | 8.00-10.00 | 2.00 |
| Mtengo wa 304N1 | 0Cr19Ni9N | 0.08 | 18.00-20.00 | 7.00-10.50 | 2.00 |
| Mtengo wa 304N2 | Mtengo wa 0Cr18Ni10NbN | 0.08 | 18.00-20.00 | 7.50-10.50 | 2.00 |
| 304LN | Mtengo wa 00Cr18Ni10N | 0.030 | 17.00-19.00 | 8.50-11.50 | 2.00 |
| 305 | 1Cr18Ni12 | 0.12 | 17.00-19.00 | 10.50-13.00 | 2.00 |
| 309s ndi | 0Cr23Ni13 | 0.08 | 22.00-24.00 | 12.00-15.00 | 2.00 |
| 310s | 0Cr25Ni20 | 0.08 | 24.00-26.00 | 19.00-22.00 | 2.00 |
| 316 | Chithunzi cha 0Cr17Ni12Mo2 | 0.08 | 16.00-18.50 | 10.00-14.00 | 2.00 |
| 1Cr18Ni12Mo2Ti6) | 0.12 | 16.00-19.00 | 11.00-14.00 | 2.00 |
| Mtengo wa 0Cr18Ni12Mo2Ti | 0.08 | 16.00-19.00 | 11.00-14.00 | 2.00 |
| 316l ndi | Chithunzi cha 00Cr17Ni14Mo2 | 0.030 | 16.00-18.00 | 12.00-15.00 | 2.00 |
| 316N | Mtengo wa 0Cr17Ni12Mo2N | 0.08 | 16.00-18.00 | 10.00-14.00 | 2.00 |
| 316N | Mtengo wa 00Cr17Ni13Mo2N | 0.030 | 16.00-18.50 | 10.50-14.50 | 2.00 |
| 316j1 | Chithunzi cha 0Cr18Ni12Mo2Cu2 | 0.08 | 17.00-19.00 | 10.00-14.50 | 2.00 |
| 316J1L | Mtengo wa 00Cr18Ni14Mo2Cu2 | 0.030 | 17.00-19.00 | 12.00-16.00 | 2.00 |
| 317 | Chithunzi cha 0Cr19Ni13Mo3 | 0.12 | 18.00-20.00 | 11.00-15.00 | 2.00 |
| 317l ndi | Mtengo wa 00Cr19Ni13Mo3 | 0.08 | 18.00-20.00 | 11.00-15.00 | 2.00 |
| Chithunzi cha 1Cr18Ni12Mo3Ti6 | 0.12 | 16.00-19.00 | 11.00-14.00 | 2.00 |
| Mtengo wa 0Cr18Ni12Mo3Ti | 0.08 | 16.00-19.00 | 11.00-14.00 | 2.00 |
| 317j1 | Chithunzi cha 0Cr18Ni16Mo5 | 0.040 | 16.00-19.00 | 15.00-17.00 | 2.00 |
| 321 | 1Cr18Ni9Ti6 | 0.12 | 17.00-19.00 | 8.00-11.00 | 2.00 |
| 0Cr18Ni10Ti | 0.08 | 17.00-19.00 | 9.00-12.00 | 2.00 |
| 347 | Mtengo wa 0Cr18Ni11Nb | 0.08 | 17.00-19.00 | 9.00-13.00 | 2.00 |
| XM7 | 0Cr18Ni9Cu3 | 0.08 | 17.00-19.00 | 8.50-10.50 | 2.00 |
| XM15J1 | 0Cr18Ni13Si4 | 0.08 | 15.00-20.00 | 11.50-15.00 | 2.00 |