| Kumparan Baja Tahan Karat Pameran Layanan Satu Atap: |
| lembaran baja tahan karat 430Komposisi Kimia dan Sifat Mekanik: |
| C% | Si% | M N% | P% | S% | Cr% | Ni% | N% | Mo% | Ti% |
| 0.12 | 1.00 | 1.00 | 0,040 | 0,030 | 16.0-18.0 | 0,75 | – | – | – |
| T*S | Y*S | Kekerasan | Pemanjangan |
| (Mpa) | (Mpa) | HRB | HB | (%) |
| 520 | 205 | – | – | 40 |
| Digulung DinginLembaran baja tahan karat 430: |
1. Kelas: seri 200 & 300
Seri 200: 201,202, J4
300 seri: 301, 304, 304L, 321, 316L, 309, 310S
2. Standar: JIS, ASTM, AISI, GB, DIN, EN, kami biasanya menggunakan Standar ASTM dan GB
3. Ketebalan: 0,14mm-3,0mm
4. Lebar: sesuai kebutuhan
5. Permukaan: 2B selesai, BA selesai
6. Kekerasan: lunak, 1/4H, 1/2H, FH
7. Toleransi Ketebalan: +/-0,02mm
8. Toleransi Lebar: +/-10mm (tepi penggilingan)
| Nilai lebih lanjut dari lembaran 430 ss: |
| Jenis | Nilai | Nilai | Komponen Kimia % |
| Baja tahan karat austenitik | | | C | Cr | Ni | Mn |
| 201 | 1Cr17Mn6Ni5N | 0,15 | Jam 16.00-18.00 | 3.50-5.50 | 5.50-7.50 |
| 201L | 03Cr17Mn6Ni5N | 0,030 | Jam 16.00-18.00 | 3.50-5.50 | 5.50-7.50 |
| 202 | 1Cr18Mn8Ni5N | 0,15 | Jam 17.00-19.00 | Jam 4.00-6.00 | Jam 7.50-10.00 |
| 204 | 03Cr16Mn8Ni2N | 0,030 | Jam 15.00-17.00 | 1,50-3,50 | Jam 7.00-9.00 |
| 1Cr18Mn10Ni5Mo3N | 0.10 | Jam 17.00-19.00 | Jam 4.00-6.00 | Jam 8.50-12.00 |
| 2Cr13Mn9Ni4 | 0,15-0,25 | Jam 12.00-14.00 | 3.70-5.00 | Jam 8.00-10.00 |
| 2Cr15Mn15Ni2N | 0,15-0,25 | Jam 14.00-16.00 | 1,50-3,00 | Jam 14.00-16.00 |
| 1Cr18Mn10Ni5Mo3N | 0,15 | Jam 17.00-19.00 | Jam 4.00-6.00 | Jam 8.50-12.00 |
| 301 | 1Cr17Ni7 | 0,15 | Jam 16.00-18.00 | Jam 6.00-8.00 | 2.00 |
| 302 | 1Cr18Ni9 | 0,15 | Jam 17.00-19.00 | Jam 8.00-10.00 | 2.00 |
| 303 | Y1Cr18Ni9 | 0,15 | Jam 17.00-19.00 | Jam 8.00-10.00 | 2.00 |
| 303se | Y1Cr18Ni9Se | 0,15 | Jam 17.00-19.00 | Jam 8.00-10.00 | 2.00 |
| 304 | 0Cr18Ni9 | 0,07 | Jam 17.00-19.00 | Jam 8.00-10.00 | 2.00 |
| 304L | 00Cr19Ni10 | 0,030 | Jam 18.00-20.00 | Jam 8.00-10.00 | 2.00 |
| 304N1 | 0Cr19Ni9N | 0,08 | Jam 18.00-20.00 | Jam 07.00-10.50 | 2.00 |
| 304N2 | 0Cr18Ni10NbN | 0,08 | Jam 18.00-20.00 | 7.50-10.50 | 2.00 |
| 304LN | 00Cr18Ni10N | 0,030 | Jam 17.00-19.00 | Jam 8.50-11.50 | 2.00 |
| 305 | 1Cr18Ni12 | 0.12 | Jam 17.00-19.00 | Jam 10.50-13.00 | 2.00 |
| 309S | 0Cr23Ni13 | 0,08 | Jam 22.00-24.00 | Jam 12.00-15.00 | 2.00 |
| 310 detik | 0Cr25Ni20 | 0,08 | Jam 24.00-26.00 | Jam 19.00-22.00 | 2.00 |
| 316 | 0Cr17Ni12Mo2 | 0,08 | Jam 16.00-18.50 | Jam 10.00-14.00 | 2.00 |
| 1Cr18Ni12Mo2Ti6) | 0.12 | Jam 16.00-19.00 | Jam 11.00-14.00 | 2.00 |
| 0Cr18Ni12Mo2Ti | 0,08 | Jam 16.00-19.00 | Jam 11.00-14.00 | 2.00 |
| 316L | 00Cr17Ni14Mo2 | 0,030 | Jam 16.00-18.00 | Jam 12.00-15.00 | 2.00 |
| 316N | 0Cr17Ni12Mo2N | 0,08 | Jam 16.00-18.00 | Jam 10.00-14.00 | 2.00 |
| 316N | 00Cr17Ni13Mo2N | 0,030 | Jam 16.00-18.50 | Jam 10.50-14.50 | 2.00 |
| 316J1 | 0Cr18Ni12Mo2Cu2 | 0,08 | Jam 17.00-19.00 | Jam 10.00-14.50 | 2.00 |
| 316J1L | 00Cr18Ni14Mo2Cu2 | 0,030 | Jam 17.00-19.00 | Jam 12.00-16.00 | 2.00 |
| 317 | 0Cr19Ni13Mo3 | 0.12 | Jam 18.00-20.00 | Jam 11.00-15.00 | 2.00 |
| 317L | 00Cr19Ni13Mo3 | 0,08 | Jam 18.00-20.00 | Jam 11.00-15.00 | 2.00 |
| 1Cr18Ni12Mo3Ti6 | 0.12 | Jam 16.00-19.00 | Jam 11.00-14.00 | 2.00 |
| 0Cr18Ni12Mo3Ti | 0,08 | Jam 16.00-19.00 | Jam 11.00-14.00 | 2.00 |
| 317J1 | 0Cr18Ni16Mo5 | 0,040 | Jam 16.00-19.00 | Jam 15.00-17.00 | 2.00 |
| 321 | 1Cr18Ni9Ti6 | 0.12 | Jam 17.00-19.00 | Jam 8.00-11.00 | 2.00 |
| 0Cr18Ni10Ti | 0,08 | Jam 17.00-19.00 | Jam 09.00-12.00 | 2.00 |
| 347 | 0Cr18Ni11Nb | 0,08 | Jam 17.00-19.00 | Jam 09.00-13.00 | 2.00 |
| XM7 | 0Cr18Ni9Cu3 | 0,08 | Jam 17.00-19.00 | 8.50-10.50 | 2.00 |
| XM15J1 | 0Cr18Ni13Si4 | 0,08 | Jam 15.00-20.00 | Jam 11.50-15.00 | 2.00 |
Sebelumnya: Pipa Las Baja Tahan Karat Berikutnya: Strip Baja Tahan Karat