AISI 310S UNS S31008 EN 1.4845
I-AISI 314 UNS S31400 EN 1.4841
Iintlobo310S SSkwaye314 SSziintsimbi ezingenasici ze-austenitic ezixutywe kakhulu ezenzelwe inkonzo kubushushu obuphezulu. Umxholo ophezulu we-Cr kunye ne-Ni uvumela le ngxubevange ukuba imelane ne-oxidation kwinkonzo eqhubekayo kubushushu obufikelela kwi-2200°F ukuba akukho zigesi zesalfure ezincitshiswayo. Kwinkonzo engapheliyo, i-310S SS ingasetyenziswa kubushushu obufikelela kwi-1900°F njengoko imelana nokukhula kwaye inomlinganiselo ophantsi wokwandiswa. Inqanaba elongeziweyo le-silicon kwi-314 SS liphucula ngakumbi ukumelana ne-oxidation kubushushu obuphezulu. I-atmosphere ye-carburizing inokunciphisa ubomi obupheleleyo kuxhomekeke kwiimeko zokwenyani. Nangona kunjalo, la manqanaba anokumelana okuphezulu xa kuthelekiswa namanqanaba aphantsi e-chromium-nickel.
Ezi klasi zisetyenziselwa ukumelana kwazo ne-oxidation kumaqondo obushushu aphezulu kwizicelo ezifana neenxalenye ze-furnace, iibhanti zokuhambisa i-furnace, ii-studs zokubamba i-insulation, njl.
IZIXHOBO EZIFUMANEKAYO
Jonga iphepha lemveliso ukuze ufumane ubungakanani, ukunyamezelana, ukugqitywa okufumanekayo kunye nezinye iinkcukacha.
Ulwakhiwo oluqhelekileyo lweeKhemikhali
| Izinto |
| C | MN | P | S | SI | CR | NI | |
| I-UNS 31000 | I-AISI 310 | Ubuncinci |
|
|
|
|
| 24.00 | 19.00 |
| Ubuninzi | 0.25 | 2.00 | 0.045 | 0.030 | 1.50 | 26.00 | 22.00 | ||
| I-UNS 31008 | I-AISI 310S | Ubuncinci |
|
|
|
|
| 24.00 | 19.00 |
| Ubuninzi | 0.08 | 2.00 | 0.045 | 0.030 | 1.50 | 26.00 | 22.00 | ||
| I-UNS 31400 | I-AISI 314 | Ubuncinci |
|
|
|
| 1.50 | 23.00 | 19.00 |
| Ubuninzi | 0.25 | 2.00 | 0.045 | 0.030 | 3.00 | 26.00 | 22.00 | ||
Iipropati zeMechanical ezibizwa ngokuba yiNominal (imeko eqhotyoshiweyo)
| Tensile strength ksi[MPa] | Unikeze Amandla ksi[MPa] | % Ukwandiswa 4d | Ukunciphisa i-% kwi Indawo |
| 95[655] | 45[310] | 50 | 60 |