Kull wieħedpjanċa tal-istainless steelgħandu l-kompożizzjoni u l-karatteristiċi kimiċi uniċi tiegħu stess, adattati għal oqsma ta' applikazzjoni differenti.
Gradi Ekwivalenti ta' Pjanċi tal-Azzar Inossidabbli 409/410/420/430/440/446
| Grad | NUMRU TAL-PRODOTT | UNS | AFNOR | BS | JIS |
| SS 409 | 1.4512 | S40900 | Z3CT12 | 409 S 19 | SUS 409 |
| SS 410 | 1.4006 | S41000 | - | 410S21 | SUS 410 |
| SS 430 | 1.4016 | S43000 | BF Z 3 CN 19-09 | - | - |
| SS 440 | 1.4125 | S44000 | - | - | - |
Kompożizzjoni Kimika ta' Pjanċi tal-Azzar Inossidabbli 409/410/420/430/440/446
| Gradi | C | Ni | Si | S | Mn | P | Cr | T i |
| SS 409 | 0.08 | 0.5 | 1.0 | 0.045 | 1.0 | 0.045 | 11.75 -10.5 | - |
| SS 410 | 0.15 massimu | 0.50 massimu | 1.0 | 0.030 | 1.0 | 0.040 | 11.5 – 13.5 | - |
| SS 430 | 0.12 | 1.0 | 0.030 | 1.0 | 0.040 | 16.0 | - | - |
| SS 440 | 0.95-1.20 | - | 1.0 | 0.030 | 1.0 | 0.040 | 16.00-18.00 | - |
PROPRJETAJIET MEKKANIĊI TAL-PJANĊI TAL-AZZAR INOSSIDABBLI 409/410/410S/420/430/440/446
| Gradi | Densità | Punt tat-Tidwib | Saħħa tat-Tensile | Saħħa tar-Rendiment (0.2%Offset) | Titwil | Ebusija (Brinell) MAX | Ebusija (Rockwell B) MAX |
| SS 409 | 8.0 g/ċm3 | 1457 °C (2650 °F) | Psi – 75000, MPa – 515 | Psi – 30000, MPa – 205 | 35% | - | - |
| SS 410 | - | 65 (450) | 30 (205) | 20 | 217 | 96 | |
| SS 430 | - | 450 | 205 | 22 | 89 | 183 | |
| SS 440 | - | 95,000 psi | 50,000 psi | 25% | 175 | - |
Ħin tal-posta: 27 ta' Ġunju 2023