Quisquelamina chalybis inoxidabilissuam compositionem chemicam et proprietates singulares habet, aptas variis applicationis locis.
Gradus Aequivalentes Laminarum Chalybis Inoxidabilis 409/410/420/430/440/446
| Gradus | OPIFICIUM NUM. | UNS | AFNOR | BS | JIS |
| SS 409 | 1.4512 | S40900 | Z3CT12 | 409 S 19 | SUS 409 |
| SS 410 | 1.4006 | S41000 | - | 410S21 | SUS 410 |
| SS 430 | 1.4016 | S43000 | BF Z 3 CN 19-09 | - | - |
| SS 440 | 1.4125 | S44000 | - | - | - |
Compositio Chemica Laminarum Chalybis Inoxidabilis 409/410/420/430/440/446
| Gradus | C | Ni | Si | S | Mn | P | Cr | T i |
| SS 409 | 0.08 | 0.5 | 1.0 | 0.045 | 1.0 | 0.045 | 11.75 - 10.5 | - |
| SS 410 | 0.15 maximum | 0.50 maximum | 1.0 | 0.030 | 1.0 | 0.040 | 11.5 – 13.5 | - |
| SS 430 | 0.12 | 1.0 | 0.030 | 1.0 | 0.040 | 16.0 | - | - |
| SS 440 | 0.95-1.20 | - | 1.0 | 0.030 | 1.0 | 0.040 | 16.00-18.00 | - |
PROPRIETATES MECHANICAE LAMINARUM CHALYBIS INOXIDABILIS 409/410/410S/420/430/440/446
| Gradus | Densitas | Punctum Liquefactionis | Robur Tensilis | Robur Cedendi (0.2%Offset) | Elongatio | Duritia (Brinell) MAX | Duritia (Rockwell B) MAX |
| SS 409 | 8.0 g/cm³ | 1457°C (2650°F) | Psi – 75000, MPa – 515 | Psi – 30000, MPa – 205 | 35% | - | - |
| SS 410 | - | LXV (CDL) | XXX (CCV) | 20 | 217 | 96 | |
| SS 430 | - | 450 | 205 | 22 | 89 | CLXXXIII | |
| SS 440 | - | 95,000 psi | 50,000 psi | XXV% | CLXXV | - |