440C tšepe e sa ruseng e bataletseng barengke sehlahisoa sa tšepe e sa hloekang sa boleng bo holimo se tsebahalang ka motsoako oa sona o ikhethang oa ho hanyetsa ho tsofala le ho hanyetsa ho bola. Ke oa lelapa la tšepe e sa hloekang ea martensitic 'me e sebelisoa haholo liindastering tse fapaneng ka lebaka la ts'ebetso ea eona e phahameng.
Maemo a Tšepe e sa Khaotseng ea 440C le Mekhahlelo ea Tšepe e Lekanang
| Naha | usa | BS le DIN | Japane |
| E tloaelehileng | ASTM A276 | EN 10088 | JIS G4303 |
| Mekhahlelo | S44004/440C | X105CrMo17/1.4125 | SUS440C |
Sebopeho sa Lik'hemik'hale tsa Tšepe sa ASTM A276 440C le tse Tšoanang
| E tloaelehileng | Sehlopha | C | Mn | P | S | Si | Cr | Mo |
| ASTM A276 | S44004/440C | 0.95-1.20 | ≦1.00 | ≦0.04 | ≦0.03 | ≦1.00 | 16.0-18.0 | ≦0.75 |
| EN10088 | X105CrMo17/1.4125 | 0.95-1.20 | ≦1.00 | ≦0.04 | ≦0.03 | ≦1.00 | 16.0-18.0 | 0.40-0.80 |
| JIS G4303 | SUS 440C | 0.95-1.20 | ≦1.00 | ≦0.04 | ≦0.03 | ≦1.00 | 16.0-18.0 | ≦0.75 |
Tšepe e sa Hlakeng ea 440CMekanikiMatlo
| Mocheso o Tekanyetsang (°C) | Matla a ho Tenyetseha (MPa) | Matla a Tlhahiso 0.2% Bopaki (MPa) | Ho lelefatsa (% ka 50mm) | Thatafalo Rockwell (HRC) | Tšusumetso Charpy V (J) |
| Annealed* | 758 | 448 | 14 | 269HB max# | - |
| 204 | 2030 | 1900 | 4 | 59 | 9 |
| 260 | 1960 | 1830 | 4 | 57 | 9 |
| 306 | 1860 | 1740 | 4 | 56 | 9 |
| 371 | 1790 | 1660 | 4 | 56 | 9 |
Mona ke lintlha tsa bohlokoa tsa ho hlahisa bare e bataletseng ea tšepe e sa hloekang ea 440C:
1. Sebopeho: 440C tšepe e sa ruseng e bataletseng e entsoe haholo-holo ka chromium (16-18%), khabone (0.95-1.20%), le likarolo tse ling tse nyane tse kang manganese, silicon le molybdenum.
2. Ho Hanela ho Tloha: Bara e bataletseng ea tšepe e sa ruseng ea 440C e tsebahala ka ho hanyetsa ho tlola ha eona ho ikhethang, e leng se etsang hore e lokele lits'ebetso tse kenyeletsang thepa e khorofo, lisebelisoa tsa ho seha, li-bearing le likarolo tse hanelang ho tsofala.
3. Ho Hanela Tshenyeho: Leha e le tshepe e sa ruseng e nang le khabone e ngata, 440C e na le kganyetso e ntle ya tshenyeho.
4. Bothata le Matla: Bara e bataletseng ea tšepe e sa ruseng ea 440C e na le bothata bo botle le matla a phahameng, e fanang ka ho tšoarella le ho phela nako e telele lits'ebetsong tse thata.
Nako ea poso: Phupu-05-2023