U'amea lamolemole 440Co se oloa u'amea e le gaoia e maualuga le tulaga lelei e lauiloa i lona tu'ufa'atasiga tulaga ese o le tete'e atu i le ofuina ma le tete'e atu i le 'ele. E patino i le aiga u'amea e le gaoia e martensitic ma e fa'aaogaina lautele i le tele o alamanuia ona o lana fa'atinoga sili ona lelei.
Tulaga Faatonuina o le 440C Stainless Steel ma Vasega U'amea Tutusa
| Atunuu | ISA | BS & DIN | Iapani |
| Tulaga Masani | ASTM A276 | EN 10088 | JIS G4303 |
| Vasega | S44004/440C | X105CrMo17/1.4125 | SUS440C |
ASTM A276 440C Fa'asologa o Kemikolo o le U'amea ma Mea Tutusa
| Tulaga Masani | Vasega | C | Mn | P | S | Si | Cr | Mo |
| ASTM A276 | S44004/440C | 0.95-1.20 | ≦1.00 | ≦0.04 | ≦0.03 | ≦1.00 | 16.0-18.0 | ≦0.75 |
| EN10088 | X105CrMo17/1.4125 | 0.95-1.20 | ≦1.00 | ≦0.04 | ≦0.03 | ≦1.00 | 16.0-18.0 | 0.40-0.80 |
| JIS G4303 | SUS 440C | 0.95-1.20 | ≦1.00 | ≦0.04 | ≦0.03 | ≦1.00 | 16.0-18.0 | ≦0.75 |
440C Uamea e le gaoiaMekanikaMeatotino
| Vevela o le Fa'amalūlūina (°C) | Malosiaga o le Fetuuna'i (MPa) | Malosiaga o le Gaosiga 0.2% Faamaoniga (MPa) | Fa'aloloa (% i le 50mm) | Ma'a'a Rockwell (HRC) | A'afiaga o le Charpy V (J) |
| Fa'a'aisa* | 758 | 448 | 14 | 269HB maualuga# | - |
| 204 | 2030 | 1900 | 4 | 59 | 9 |
| 260 | 1960 | 1830 | 4 | 57 | 9 |
| 306 | 1860 | 1740 | 4 | 56 | 9 |
| 371 | 1790 | 1660 | 4 | 56 | 9 |
O nisi nei o manatu autu e faʻalauiloa ai le uʻamea e le gaoia 440C:
1. Fa'atulagaga: O le u'amea e le gaoia 440C e tele lava ina faia i le chromium (16-18%), carbon (0.95-1.20%), ma ni nai vaega o isi elemene e pei o le manganese, silicon, ma le molybdenum.
2. Tete'e i le Ofu: O le u'amea e le gaoia 440C e lauiloa i lona tete'e tele i le ofu, ma e talafeagai ai mo fa'aoga e aofia ai mea e olo ai, meafaigaluega tipi, u'amea, ma vaega e tete'e i le ofu.
3. Tete'e atu i le 'Ele: E ui o se u'amea e le gaoia e maualuga le kaponi, ae e lelei le tete'e atu o le 440C i le 'ele.
4. Ma'a'a ma le Malosi: O le u'amea e le gaoia 440C e matua'i ma'a'a ma malosi tele, e tumau ma umi se taimi e fa'aoga ai.
Taimi na lafoina ai: Iulai-05-2023