Ba plat an asye pur 440Cse yon pwodwi asye pur kalite siperyè ki li te ye pou konbinezon eksepsyonèl li nan rezistans mete ak rezistans korozyon. Li fè pati fanmi asye pur martensitik la epi li lajman itilize nan divès endistri pou pèfòmans siperyè li.
Estanda pou asye pur 440C ak klas asye ekivalan
| Peyi | Etazini | BS ak DIN | Japon |
| Estanda | ASTM A276 | AN 10088 | JIS G4303 |
| Nòt yo | S44004/440C | X105CrMo17/1.4125 | SUS440C |
Konpozisyon Chimik ak Ekivalan Asye ASTM A276 440C
| Estanda | Klas | C | Mn | P | S | Si | Cr | Mo |
| ASTM A276 | S44004/440C | 0.95-1.20 | ≤1.00 | ≤0.04 | ≤0.03 | ≤1.00 | 16.0-18.0 | ≤0.75 |
| EN10088 | X105CrMo17/1.4125 | 0.95-1.20 | ≤1.00 | ≤0.04 | ≤0.03 | ≤1.00 | 16.0-18.0 | 0.40-0.80 |
| JIS G4303 | SUS 440C | 0.95-1.20 | ≤1.00 | ≤0.04 | ≤0.03 | ≤1.00 | 16.0-18.0 | ≤0.75 |
Asye pur 440CMekanikPwopriyete
| Tanperati Revenu (°C) | Fòs tansyon (MPa) | Fòs sede 0.2% Prèv (MPa) | Elongasyon (% nan 50mm) | Dite Rockwell (HRC) | Enpak Charpy V (J) |
| Rekwit* | 758 | 448 | 14 | 269HB maksimòm # | - |
| 204 | 2030 | 1900 | 4 | 59 | 9 |
| 260 | 1960 | 1830 | 4 | 57 | 9 |
| 306 | 1860 | 1740 | 4 | 56 | 9 |
| 371 | 1790 | 1660 | 4 | 56 | 9 |
Men kèk pwen kle pou prezante ba plat asye pur 440C:
1. Konpozisyon: Ba plat asye pur 440C a konpoze prensipalman de chromium (16-18%), kabòn (0.95-1.20%), ak ti kantite lòt eleman tankou Manganèz, Silisyòm, ak molybdenum.
2. Rezistans Mete: Ba plat asye pur 440C a renome pou rezistans eksepsyonèl li nan mete, sa ki fè li apwopriye pou aplikasyon ki enplike materyèl abrazif, zouti koupe, kousinen, ak konpozan ki reziste mete.
3. Rezistans korozyon: Malgre ke li se yon asye pur ki gen anpil kabòn, 440C montre bon rezistans korozyon.
4. Dite ak Fòs: Ba plat asye pur 440C a gen yon dite ekselan ak yon gwo fòs, sa ki bay rezistans ak lonjevite nan aplikasyon ki mande anpil.
Dat piblikasyon: 5 Jiyè 2023