Distingue inter proprietates functionis chalybis inoxidabilis 420, 420J1 et 420J2:
Differentia principalis inter chalybem inoxidabilem 420J1 et 420J2
420J1 certum gradum resistentiae attritionis et corrosionis, duritiem magnam, et pretium eius inferius est inter sphaeras chalybis inoxidabilis. Apta est ad ambitum laboris ubi chalybs inoxidabilis ordinarius requiritur.
Cingulum chalybis inoxidabilis 420J2 est genus chalybis inoxidabilis productum secundum normas Americanas ASTM; normam Iaponicam SUS420J2, novam normam nationalem 30Cr13, vetus normam nationalem 3Cr13, codicem digitalem S42030, et normam Europaeam 1.4028.
Chalybs inoxidabilis 420J1: Post refrigerationem, durities alta est, et resistentia corrosionis bona (magnetica). Post refrigerationem, chalybs inoxidabilis 420J2 durior est quam chalybs 420J1 (magneticus).
Generaliter, temperatura refrigerationis 420J1 est 980~1050℃. Durities refrigerationis olei calefactionis 980℃ significanter inferior est quam refrigerationis olei calefactionis 1050℃. Durities post refrigerationem olei 980℃ est HRC45-50, et durities post refrigerationem olei 1050℃ est 2HRC altior. Attamen microstructura post refrigerationem ad 1050℃ obtenta crassa et fragilis est. Ad meliorem structuram et duritias obtinendas, calefactio et refrigeratio 1000℃ commendatur.
Laminae et Bracteae Chalybis Inoxidabilis 420 / 420J1 / 420J2, Gradus Aequivalentes:
| NORMA | JIS | OPUS NUM. | BS | AFNOR | SIS | UNS | AISI |
| SS 420 | SUS 420 | 1.4021 | 420S29 | - | 2303 | S42000 | 420 |
| Inoxidabilis 420J1 | SUS 420J1 | 1.4021 | 420S29 | Z20C13 | 2303 | S42010 | 420L |
| Inoxidabilis 420J2 | SUS 420J2 | 1.4028 | 420S37 | Z20C13 | 2304 | S42010 | 420M |
SS420 / 420J1/ 420J2 Laminae, Tabulae Compositio Chemica (chalybs saky):
| Gradus | C | Mn | Si | P | S | Cr | Ni | Mo |
| SUS 420 | 0.15 maximum | 1.0 maximum | 1.0 maximum | 0.040 maximum | 0.030 maximum | 12.0-14.0 | - | - |
| SUS 420J1 | 0.16-0.25 | 1.0 maximum | 1.0 maximum | 0.040 maximum | 0.030 maximum | 12.0-14.0 | - | - |
| SUS 420J2 | 0.26-0.40 | 1.0 maximum | 1.0 maximum | 0.040 maximum | 0.030 maximum | 12.0-14.0 | - | - |
SS 420 420J1 420J2 Laminae, Tabulae Proprietates mechanicae (chalybs saky):
| Gradus | Robur Tensilis Maximum | Robur Cedendi (0.2%Offset) Maximum | Elongatio (in 2 unc.) |
| 420 | MPa – 650 | MPa – 450 | 10% |
| 420J1 | MPa – 640 | MPa – 440 | XX% |
| 420J2 | MPa – 740 | MPa – 540 | 12% |
Durities chalybis seriei 420 post curationem caloris est circiter HRC52~55, et effectus variorum aspectuum, ut resistentia damni, non admodum egregius est. Quia facilius secatur et politur, aptus est ad productionem cultrorum. Chalybs inoxidabilis 420 etiam chalybs martensiticus "gradus secandi" appellatur. Chalybs seriei 420 excellentem resistentiam rubigini habet propter parvum contentum carbonis (contentum carbonis: 0.16~0.25), itaque chalybs idealis est ad productionem instrumentorum urinantium.