A182-F11, A182-F12, sareng A182-F22 mangrupikeun sasmita tina baja alloy anu biasa dianggo pikeun sagala rupa aplikasi industri, khususna dina lingkungan suhu luhur sareng tekanan tinggi.sasmita ieu mibanda komposisi kimiawi béda jeung sipat mékanis, sahingga cocog pikeun tipena béda applications.They utamana dipaké dina sistem tekanan, kaasup flanges, fittings, valves jeung bagian sarupa, sarta loba dipaké dina pabrik pétrokimia, konversi batubara, kakuatan nuklir, silinder turbin uap, kakuatan termal jeung parabot skala badag lianna kalayan kaayaan operasi kasar jeung média corrosive kompléks.
F11 BAJA KOMPOSISI KIMIATION
| Tingkat | Kelas | C | Si | Mn | P | S | Cr | Mo |
| Kelas 1 | F11 | 0.05-0.15 | 0.5-1.0 | 0.3-0.6 | ≤0.03 | ≤0.03 | 1.0-1.5 | 0.44-0.65 |
| Kelas 2 | F11 | 0.1-0.2 | 0.5-1.0 | 0.3-0.6 | ≤0.04 | ≤0.04 | 1.0-1.5 | 0.44-0.65 |
| Kelas 3 | F11 | 0.1-0.2 | 0.5-1.0 | 0.3-0.6 | ≤0.04 | ≤0.04 | 1.0-1.5 | 0.44-0.65 |
F12 BAJA KOMPOSISI KIMIATION
| Tingkat | Kelas | C | Si | Mn | P | S | Cr | Mo |
| Kelas 1 | F12 | 0.05-0.15 | ≤0.5 | 0.3-0.6 | ≤0,045 | ≤0,045 | 0.8-1.25 | 0.44-0.65 |
| Kelas 2 | F12 | 0.1-0.2 | 0.1-0.6 | 0.3-0.8 | ≤0.04 | ≤0.04 | 0.8-1.25 | 0.44-0.65 |
F22 BAJA KOMPOSISI KIMIATION
| Tingkat | Kelas | C | Si | Mn | P | S | Cr | Mo |
| Kelas 1 | F22 | 0.05-0.15 | ≤0.5 | 0.3-0.6 | ≤0.04 | ≤0.04 | 2.0-2.5 | 0.87-1.13 |
| Kelas 3 | F22 | 0.05-0.15 | ≤0.5 | 0.3-0.6 | ≤0.04 | ≤0.04 | 2.0-2.5 | 0.87-1.13 |
F11 / F12 / F22 STEEL sipat mékanis
| Kelas | Tingkat | Kakuatan Tensile, Mpa | Kakuatan ngahasilkeun, Mpa | Elongasi,% | Ngurangan Wewengkon,% | Teu karasa, HBW |
| F11 | Kelas 1 | ≥415 | ≥205 | ≥20 | ≥45 | 121-174 |
| Kelas 2 | ≥485 | ≥275 | ≥20 | ≥30 | 143-207 | |
| Kelas 3 | ≥515 | ≥310 | ≥20 | ≥30 | 156-207 | |
| F12 | Kelas 1 | ≥415 | ≥220 | ≥20 | ≥45 | 121-174 |
| Kelas 2 | ≥485 | ≥275 | ≥20 | ≥30 | 143-207 | |
| F22 | Kelas 1 | ≥415 | ≥205 | ≥20 | ≥35 | ≤170 |
| Kelas 3 | ≥515 | ≥310 | ≥20 | ≥30 | 156-207 |
Beda utama antara baja alloy A182-F11, A182-F12, sareng A182-F22 perenahna dina komposisi kimiana sareng sipat mékanis anu dihasilkeun.A182-F11 nawiskeun kinerja anu saé dina suhu sedeng, sedengkeun A182-F12 sareng A182-F22 nyayogikeun kakuatan anu langkung luhur sareng résistansi kana korosi sareng ngarayap suhu luhur, sareng A182-F22 umumna mangrupikeun anu paling kuat sareng paling tahan korosi diantara tilu.