Okùn Irin Alagbara Ti a Yipo Tutu
Àpèjúwe Kúkúrú:
| Ifihàn Iṣẹ́ Ìdádúró Kan: |
| Ìṣètò Kẹ́míkà àti Àwọn Ohun Èlò Ìdánilẹ́kọ̀ọ́ |
| C% | Si% | Mn% | P% | S% | Cr% | Kòsí% | N% | Oṣù% | Tí% |
| 0.08 | 0.75 | 2.0 | 0.045 | 0.030 | 18.0-20.0 | 8.0-10.5 | 0.10 | – | – |
| T*S | Y*S | Líle | Gbigbọn | |
| (Mpa) | (Mpa) | HRB | HB | (%) |
| 520 | 205 | – | – | 40 |
| Àpèjúwe ti ìkòkò irin alagbara tí a fi irin ṣe tí a fi irin tútù rọ̀: |
| Àpèjúwe | Irin okun alagbara ti a yipo tutu |
| Ohun èlò | 201, 202,304, 304L, 316, 316L, 317, 317L, 321, 347H, 309, 309S, 310, 310S, 410, 420, 430, àti bẹ́ẹ̀ bẹ́ẹ̀ lọ |
| boṣewa | ASTM A240, JIS G4304, G4305, GB/T 4237, GB/T 8165, BS 1449, DIN17460, DIN 17441 |
| Iwọn | Sisanra: 0.03-3mm Fífẹ̀: 8-600mm, |
| Ipari dada | 2B, BA, 2D, Nọ́mbà 1, Nọ́mbà 4, Nọ́mbà 8, 8K, (dígí), tí a ti dán, HL (ìlà irun), àti bẹ́ẹ̀ bẹ́ẹ̀ lọ |
| Ohun elo | a) Àwọn ilé iṣẹ́ iṣẹ́ gbogbogbòò (epo, oúnjẹ, kẹ́míkà, ìwé, ajílẹ̀, aṣọ, ọkọ̀ òfúrufú àti nuclear) b) Gbigbe titẹ ati ooru c) Ikole ati ohun ọṣọ |
| Àpò | Okeere boṣewa package: apoti onigi ti a fi papọ tabi o nilo; |
| Akoko Ifijiṣẹ | Gẹ́gẹ́ bí iye àwọn oníbàárà. |
| Ìsanwó | T/T, L/C, àti Western Union |
| Ọjà | Yúróòpù, Gúúsù Amẹ́ríkà, Áfíríkà, Òkun, bíi: Orílẹ̀-èdè Amẹ́ríkà, Jámánì, Íńdíà, Ìrán, Dúbáì, Íráàkì, Fíétnámì, Irélíà, Singapore, ati bẹbẹ lọ |
| Awọn ipele diẹ sii tiIrin alagbara ti a yipo tutu: |
| Ipele | Si | Mn | p | S | Cr | Mo | Ni | miiran |
| 201 | 0.15 | 1.00 | 5.5-7.5 | 0.06 | 0.03 | 16-18 | - | 1.0 |
| 202 | 0.15 | 1.00 | 7.5-10.0 | 0.06 | 0.03 | 17-19 | - | 4.0-6.0 |
| 301 | 0.15 | 1.00 | 2.00 | 0.045 | 0.03 | 16-18 | - | 6.0-8.0 |
| 304 | 0.08 | 1.00 | 2.00 | 0.045 | 0.03 | 18-20 | - | 8-10.5 |
| 304l | 0.03 | 1.00 | 2.00 | 0.045 | 0.03 | 18-20 | - | 9-13 |
| 309s | 0.08 | 1.00 | 2.00 | 0.045 | 0.03 | 22-24 | - | 12-15 |
| Àwọn ọdún 310 | 0.08 | 1.5 | 2.00 | 0.045 | 0.03 | 24-26 | - | 19-22 |
| 316 | 0.03 | 1.00 | 2.00 | 0.045 | 0.03 | 16-18 | 2-3 | 10-14 |
| 316L | 0.03 | 1.00 | 2.00 | 0.045 | 0.03 | 16-18 | 2-3 | 12-15 |
| 321 | 0.08 | 1.00 | 2.00 | 0.045 | 0.03 | 17-19 | - | 9-13 |
| 430 | 0.12 | 0.75 | 1.00 | 0.04 | 0.03 | 16-18 | - | =0.6 |