Spira Chalybis Inoxidabilis Frigida Laminata
Descriptio Brevis:
| Speculae Chalybis Inoxidabilis Una Statio Servitii Exhibitio: |
| Compositio Chemica et Proprietates Mechanicae |
| C% | Si% | Mn% | P% | S% | Cr% | Ni% | N% | Mo% | Ti% |
| 0.08 | 0.75 | 2.0 | 0.045 | 0.030 | 18.0-20.0 | 8.0-10.5 | 0.10 | – | – |
| T*S | Y*S | Duritia | Elongatio | |
| (Mpa) | (Mpa) | HRB | HB | (%) |
| 520 | 205 | – | – | 40 |
| Descriptio cochleae chalybis inoxidabilis frigidae laminatae: |
| Descriptio | Coil chalybis inoxidabilis frigide laminatus |
| Materia | 201, 202, 304, 304L, 316, 316L, 317, 317L, 321, 347H, 309, 309S, 310, 310S, 410, 420, 430, etc. |
| norma | ASTM A240, JIS G4304, G4305, GB/T 4237, GB/T 8165, BS 1449, DIN 17460, DIN 17441 |
| Magnitudo | Crassitudo: 0.03-3mm Latitudo: 8-600mm, |
| Superficies ornata | 2B, BA, 2D, No. 1, No. 4, No. 8, 8K, (speculum), politum, HL (capillitium), etc. |
| Applicatio | a) Industriae servitiorum generalium (petroleum, cibus, chemia, charta, stercora, textilia, aviatio et nuclearis) b) Pressio et transmissio caloris c) Constructio et ornamentum |
| Sarcina | Sarcina norma exportanda: arca lignea inclusa vel requirenda; |
| Tempus traditionis | Secundum quantitatem emptoris. |
| Solutio | T/T, L/C, et Western Union |
| Mercatus | Europa, America Meridionalis, Africa, Oceania, ut puta: Civitates Foederatae Americae, Germania, India, Irania, Dubai, Iraquia, Vietnamia, Hibernia Singapura, et cetera |
| Plures gradusCopula chalybis inoxidabilis frigida laminata: |
| Gradus | Si | Mn | p | S | Cr | Mo | Ni | alius |
| 201 | 0.15 | 1.00 | 5.5-7.5 | 0.06 | 0.03 | XVI-XVIII | - | 1.0 |
| 202 | 0.15 | 1.00 | 7.5-10.0 | 0.06 | 0.03 | XVII-XIX | - | 4.0-6.0 |
| 301 | 0.15 | 1.00 | 2.00 | 0.045 | 0.03 | XVI-XVIII | - | 6.0-8.0 |
| 304 | 0.08 | 1.00 | 2.00 | 0.045 | 0.03 | XVIII-XX | - | 8-10.5 |
| 304l | 0.03 | 1.00 | 2.00 | 0.045 | 0.03 | XVIII-XX | - | 9-13 |
| 309s | 0.08 | 1.00 | 2.00 | 0.045 | 0.03 | XXII-XXIV | - | XII-XV |
| 310s | 0.08 | 1.5 | 2.00 | 0.045 | 0.03 | XXIV-XXVI | - | XIX-XXII |
| CCCXVI | 0.03 | 1.00 | 2.00 | 0.045 | 0.03 | XVI-XVIII | 2-3 | 10-14 |
| 316L | 0.03 | 1.00 | 2.00 | 0.045 | 0.03 | XVI-XVIII | 2-3 | XII-XV |
| 321 | 0.08 | 1.00 | 2.00 | 0.045 | 0.03 | XVII-XIX | - | 9-13 |
| 430 | 0.12 | 0.75 | 1.00 | 0.04 | 0.03 | XVI-XVIII | - | =0.6 |