Hastelloy C-4
Inkcazelo emfutshane:
I-Hastelloy C-4 (UNS NO6455)
Iimpawu zeHastelloy C-4 kunye neSishwankathelo seSicelo:
Ingxubevange yi austenitic low-carbon nickel-molybdenum-chromium alloy.Umahluko ophambili phakathi kwe-Nicrofer 6616 hMo kunye nezinye ii-alloys zemichiza efanayo ephuhliswe ngaphambili yikhabhoni ephantsi, i-silicon, isinyithi kunye ne-tungsten.Olu qulunqo lweekhemikhali lubonelela ngozinzo olugqwesileyo kwi-650-1040 ° C kunye nokuphucula ukuxhathisa kwi-corrosion intergranular, ukuphepha ukuxhatshazwa kwe-edge line kunye ne-weld HAZ corrosion phantsi kweemeko ezifanelekileyo zokuvelisa.I-alloy esetyenziswe kwiinkqubo ze-flue gas desulfurization, i-pickling kunye ne-acid regeneration plant, i-acetic acid kunye nokuveliswa kweekhemikhali zezolimo, ukuveliswa kwe-titanium dioxide (indlela ye-chloride), i-electrolytic plating.
IHastelloy C-4 Iibrendi ezifanayo:
I-NS335 (eTshayina) W.Nr.2.4610 NiMo16Cr16Ti (eJamani)
IHastelloy C-4 Ukwakheka kwemichiza:
| Ingxubevange | % | Ni | Cr | Fe | Mo | Nb | Co | C | Mn | Si | S | Cu | Al | Ti |
| Hastelloy C-4 | Min | Umda | 14.5 | 14.0 | ||||||||||
| Ubuninzi | 17.5 | 3.0 | 17.0 | 2.0 | 0.009 | 1.0 | 0.05 | 0.01 | 0.7 |
Hastelloy C-4 iiPropati zoMzimba:
| Ukuxinana | Indawo yokunyibilika | I-Thermal conductivity | Umthamo wobushushu obuthile | Imodyuli ye-elastic | Shear imodyuli | Ukuxhathisa | Umlinganiselo wePoisson | I-coefficient yokwandiswa komgca |
| 8.6 | 1335 | 10.1(100℃) | 408 | 211 | 1.24 | 10.9(100℃) |
IiPropati zoomatshini zeHastelloy C-4: (ubuncinane beempawu zoomatshini kuma-20 ℃):
| Iindlela zonyango lobushushu | Amandla okuqina σb/MPa | Isivuno Amandlasp0.2/MPa | Umlinganiselo wobude σ5 /% | Brinell ubulukhuni HBS |
| Unyango lwesisombululo | 690 | 275 | 40 |
Imigangatho yemveliso yeHastelloy C-4:
| Umgangatho | Ibha | Forgings | Icwecwe (nge) imathiriyeli | Ucingo | Umbhobho |
| Umbutho waseMelika woVavanyo kunye neMathiriyeli | I-ASTM B574 | I-ASTM B336 | I-ASTM B575 | I-ASTM B622 | |
| I-American Aerospace Materials Specification yobuchwephesha | |||||
| Umbutho waseMelika weeNjineli zeMechanical | ASME SB574 | ASME SB336 | ASME SB575 | I-ASTM SB622 |
Inkqubo yokusebenza kweHastelloy C-4 kunye neemfuno:
I-1, kwinkqubo yonyango lobushushu ayikwazi ukudibana nesalfure, i-phosphorus, ilothe kunye nezinye iindawo eziphantsi zokunyibilika kwesinyithi, okanye i-alloy iya kuba yi-brittle, kufuneka ithathele ingqalelo ukususa njengepeyinti yokumakisha, ipeyinti yesalathisi sobushushu, iikhrayoni ezinemibala, izithambiso, amafutha. kunye nokunye ukungcola.I-sulfur content ye-fuel ingcono, umxholo wesulfure wegesi yendalo kufuneka ube ngaphantsi kwe-0.1%, umxholo wesulfure weoli enzima kufuneka ube ngaphantsi kwe-0.5%.Ukufudumala kwesithando sombane kukhetho olungcono, kuba isithando sombane sinokulawula ngokuchanekileyo ubushushu kunye negesi yomlilo ihlambulukile.Ukuba igesi yesitovu segesi icocekile ngokwaneleyo, ungakhetha.
2, i-alloy processing thermal iqondo lobushushu boluhlu lwe-1080 ℃ ~ 900 ℃, indlela yokupholisa yokupholisa kwamanzi okanye okunye ukupholisa ngokukhawuleza.Ukuqinisekisa ukuxhathisa kwe-corrosion, unyango lobushushu kufuneka lwenziwe emva kokulungiswa kobushushu besisombululo.